Description
This 0.2mm Fluorocarbon-Coated Wood Pattern Pre-Painted Aluminum Coil, featuring oak wood texture, is custom-made for commercial space wall decoration panels. Its ultra-thin 0.2mm thickness ensures flexibility, easily adapting to curved or irregular wall surfaces in malls, restaurants, or office lobbies.
The premium fluorocarbon coating delivers strong resistance to scratches, stains, and daily wear—ideal for high-traffic commercial areas. The realistic oak texture mimics natural wood warmth while avoiding wood’s drawbacks of warping or rotting. Lightweight and easy to install, it cuts construction time. It meets commercial decoration’s aesthetic and durability needs, blending natural style with long-lasting performance for eye-catching wall finishes.
Paint Performance
| Test Item | Paint |
| PVDF | PE And Others |
| With Varnish | Without Varnish |
| Paint Film Thickness, μ | ≥22 | ≥30 | ≥18 |
| Shine Tolerance | Shine≥80 Unit, ±10 Unit Allowed |
| Shine≥20-80 Unit, ±7 Unit Allowed |
| Shine<20 Unit, ±5 Unit Allowed |
| Pencil Hardness | ≥1H |
| Abrasion Resistance, L/μm | ≥5 | -- |
| T-bend | ≤2T | ≤3T |
| Impact Strength | 50KG.CM Without Depainting And Crack |
| Adhesive Force (Class) | ≥1 |
| Boiling Water Resistance | Unvarying |
| Chemical Resistance | Acid Endurance | Unvarying |
| Alkali Stability | Unvarying |
| Oil Resistivity | Unvarying |
| Resistance To Solvent | ≥70 | ≥50 |
| Scrub Resistance | ≥10000 Times Unvarying |
| Dirt Resistance | ≤15% | -- |
| Salt Spray Resistance(class) | ≥ 2 class | -- |
Features
0.2mm ultra-thin: Flexible for curved/irregular walls
Fluorocarbon coating: Resists scratches, stains, wear
Realistic oak texture: Mimics natural wood warmth
Anti-warp/rot: Overcomes natural wood flaws
Lightweight: Easy to install, cuts construction time
Custom for commercial spaces: Ideal for high-traffic areas (malls, lobbies)